specifcations subject to change without notice. please check our website for latest information. 200c power inductors at563pka 3316 power inductor core material ferrite terminations tin-silver-copper over copper weight 0.95 C 1.25 g ambient temperature C55c to +140c with i rms current, +140c to +200c with derated current storage temperature component: C55c to +200c. packaging: C55c to +80c resistance to soldering heat max three 40 second refows at +260c, parts cooled to room temperature between cycles moisture sensitivity level (msl) 1 (unlimited foor life at <30c / 85% relative humidity) enhanced crush-resistant packaging 750 per 13 reel plastic tape: 24 mm wide, 0.35 mm thick, 12 mm pocket spacing, 6.4 mm pocket depth high temperature materials allow operation in ambient temperatures up to 200c. soldered self-leaded construction for excellent solderability. very low dcr values and excellent current handling 1. when ordering, specify testing code: at563pka301ml z testing: z = cots h = screening per coilcraft cp-sa-10001 n = screening per coilcraft cp-sa-10004 2. inductance tested at 100 khz, 0.1 vrms, 0 adc using an agilent/hp 4263b lcr meter or equivalent. 3. srf measured using agilent/ hp 8753d network analyzer or equivalent.. 4. typical dc current at which the inductance drops 10% (typ) from its value without current. 5. typical current that causes a 40c temperature rise from 25c ambient. 6. electrical specifcations at 25c. refer to doc 362 soldering surface mount components before soldering. dcr srf isat (a) 4 irms (a) 5 inductance 2 (mohm) (mhz) 3 10% 20% 30% 20c 40c part number 1 20% (h) typ max min typ drop drop drop rise rise at563pka301mlz 0.3 2.6 3.0 200 238 14.0 16.0 17.0 8.0 12.0 at563pka901mlz 0.9 5.1 6.0 122 153 8.6 10.2 10.9 6.1 8.8 at563pka122mlz 1.2 5.1 6.0 100 125 7.0 8.4 9.3 3.4 5.6 at563pka182mlz 1.8 7.7 9.0 86 108 6.2 7.4 8.1 3.2 5.0 at563pka222mlz 2.2 6.8 10 74 92 6.0 6.7 7.2 2.9 4.5 AT563PKA272MLZ 2.7 9.4 11 63 79 5.1 6.0 6.4 2.7 4.2 at563pka332mlz 3.3 11.1 13 57 71 4.7 5.5 6.0 2.4 4.0 at563pka392mlz 3.9 15.3 18 54 68 4.3 5.2 5.5 2.4 4.0 at563pka472mlz 4.7 20.4 24 46 57 4.0 4.4 4.8 2.4 3.7 at563pka562mlz 5.6 21.3 25 43 53 3.6 4.1 4.4 2.2 3.3 at563pka682mlz 6.8 25.5 30 38 48 3.3 3.7 4.0 2.2 3.3 at563pka822mlz 8.2 29.8 35 35 44 2.9 3.4 3.7 2.2 3.2 at563pka103mlz 10 32.3 38 30 38 2.7 3.1 3.4 2.1 3.1 at563pka123mlz 12 40.8 48 26 33 2.5 2.9 3.1 1.7 2.7 at563pka153mlz 15 49.3 58 25 31 2.2 2.5 2.8 1.9 2.6 at563pka183mlz 18 59.5 70 21 27 2.1 2.4 2.6 1.9 2.5 at563pka223mlz 22 72.3 85 20 25 1.9 2.1 2.3 1.8 2.4 at563pka273mlz 27 85 100 19 24 1.7 1.9 2.1 1.3 1.9 at563pka333mlz 33 109 128 16 20 1.5 1.7 1.9 1.3 1.8 at563pka393mlz 39 116 136 14 18 1.3 1.5 1.7 1.3 1.8 at563pka473mlz 47 146 172 12 15 1.2 1.4 1.5 1.1 1.5 at563pka563mlz 56 170 200 11 14 1.1 1.3 1.4 0.9 1.3 at563pka683mlz 68 221 260 10 13 0.85 1.2 1.3 0.82 1.2 at563pka823mlz 82 264 310 9.5 12 0.82 1.1 1.2 0.81 1.2 at563pka104mlz 100 306 360 8.3 10 0.80 0.96 1.1 0.80 1.1 at563pka124mlz 120 384 452 8.3 10 0.70 0.85 0.98 0.68 0.90 at563pka154mlz 150 432 508 7.0 8.7 0.65 0.80 0.86 0.63 0.87 document at196-1 revised 04/22/11 ? ? coilcraft, inc. 2012 1102 silv er lak e road car y, il 60013 phone 800-981-0363 fa x 847-639-1508 email c ps@coilcraft.com www . coilcraft-cps . com this pr oduct may not be used in medical or hig h risk applications without prior coilcraft appr oval. specifications subject to change without notice. please check our web site for latest infor mation.
at563pka series (3316) 3316 power inductor irms derating dimensions are in inches mm recommended land p attern 0.060 1,52 0.160 4,06 0.330 8,38 0.400 10,16 0.390 9,91 max 0.225 5,71 max 0.150 3,81 0.120 3,05 typ 0.520 13,21 0.460 11,68 max max 0.360 9.14 min dot indicates star t document at196-2 revised 04/22/11 ? ? coilcraft, inc. 2012 1102 silv er lak e road car y, il 60013 phone 800-981-0363 fa x 847-639-1508 email c ps@coilcraft.com www . coilcraft-cps . com this pr oduct may not be used in medical or hig h risk applications without prior coilcraft appr oval. specifications subject to change without notice. please check our web site for latest infor mation.
|
